介孔碳材料的制備及其分離四環(huán)素的性能研究
Preparation of mesoporous carbon material and its separation performance of tetracycline

1.4萬(wàn)字 34頁(yè) 原創(chuàng)作品，已通過(guò)查重系統(tǒng)


目錄
第一章 緒論..............................................1
1.1前言.......................................................1
1.2多孔碳材料.................................................1
1.2.1多孔碳材料的制備方法.....................................1
1.2.2介孔碳材料...............................................4
1.3介孔碳材料的合成方法.......................................4
1.3.1 CMK-1....................................................4
1.3.2 CMK-3....................................................4
1.3.3 CMK-5....................................................6
1.4介孔碳的應(yīng)用................................................8
1.4.1 催化劑載體...............................................8
1.4.2 模板材料.................................................8
1.4.3 生物大分子的吸附和分離載體...............................9
1.4.4 生物醫(yī)藥領(lǐng)域.............................................9
1.4.5 環(huán)境領(lǐng)域.................................................9
1.4.6 電化學(xué)領(lǐng)域和能量?jī)?chǔ)存領(lǐng)域................................10
1.5應(yīng)用前景...................................................10
第2章 介孔碳材料的制備與表征...........................13
2.1 前言.......................................................13
2.2 介孔碳材料的合成路線.......................................13
2.3 試劑.......................................................14
2.4 以葡萄糖為碳源合成介孔碳材料...............................14
2.4.1 介孔碳材料合成...........................................14
2.4.2 氫氧化鉀活化.............................................15
2.4.3 介孔碳材料的吸附動(dòng)力學(xué)性能測(cè)定...........................15
2.4.4 介孔碳材料的吸附等溫線的繪制.............................15
2.4.5材料表征.................................................16
第三章 葡萄糖介孔碳材料應(yīng)用的研究.......................17
3.1葡萄糖介孔碳材料的表征....................................17
3.1.1 SEM和TEM電鏡圖........................................17
3.1.2 紅外光譜圖.............................................18
3.1.3 N2的吸附-脫附曲線......................................18
3.1.4 小結(jié)...................................................29
3.2 介孔碳材料及研究.........................................20
3.2.1 溶液初始 pH 對(duì)吸附的影響...............................21
3.2.2 靜態(tài)吸附實(shí)驗(yàn)...........................................21
3.3 吸附等溫線...............................................23
3.4 吸附動(dòng)力學(xué)...............................................23
3.5 介孔碳材料的再生性能.....................................24
3.6 小結(jié).....................................................25

結(jié)論....................................................26
致謝....................................................27
參考文獻(xiàn)................................................28


摘要 有序介孔材料的孔道結(jié)構(gòu)高度有序，孔徑尺寸可以調(diào)控，具有較好的熱穩(wěn)定性和耐水解性以及高的比表面積，在多相催化、吸附、分離、生物材料、傳感器新型復(fù)合材料等眾多領(lǐng)域有廣泛的應(yīng)用前景。本文設(shè)計(jì)合成了基于葡萄糖為碳源的新型高分子介孔碳材料，并從UV-Vis吸收光譜等方面研究了其對(duì)四環(huán)素類(lèi)抗生素的分離性能經(jīng)行了一系列研究。主要結(jié)果如下：
1、通過(guò)以葡萄糖為碳源、埃洛石為模板成功合成了新型介孔碳材料。并通過(guò)TEM、SEM等一系列表征手段確定其結(jié)構(gòu)。
2、通過(guò)以活化后的介孔碳材料對(duì)鹽酸四環(huán)素進(jìn)行分離探究，采用UV-Vis吸收光譜進(jìn)行分析，確定該材料對(duì)四環(huán)素類(lèi)抗生素具有顯著的分離效果。
3、通過(guò)運(yùn)用Origin，Uvprobe，Omnic等軟件學(xué)習(xí)繪制介孔碳材料對(duì)鹽酸四環(huán)素吸附的動(dòng)力學(xué)曲線以及等溫吸附曲線。



關(guān)鍵詞：介孔碳，葡萄糖，四環(huán)素，吸附分離